Description
Chemical Composition
| Silicon Dioxide | SiO2 | 19.41% |
| Aluminum Oxide | AL2O3 | 5.85% |
| Ferric Oxide | Fe2O3 | 3.54% |
| Calcium Oxide | CaO | 64.53% |
| Magnesium Oxide (Max 5.0) | MgO | 0.72% |
| Sulfur Trioxide (Max 4.0) | SO3 | 2.75% |
| Chloride <0.10 | CL-<0.1 | 0.013% |
| Insoluble residue (Max 5.0) | L.O.I | 0.21% |
| Loss on ignition (Max 5.0) | I.R | 3.57% |
| Free-Lime<2 | F-CaO < 2 | 0.6% |
| Chromium hexavalent (Max2.0) | Cr VI<2 | 1.2 ppm |
Physics Test
| Fineness (Blaine) | 3630cm2/g | |
| Water consistency | 26.2% | |
| Initial setting time | Min 45 | 166 minutes |
| Final setting time | 214 minutes | |
| 2 day flexural | 5.2MPa | |
| 2 day (compressive strength) | Min 20 | 23.9MPa |
| 28 day flexural | 8.9MPa | |
| 28 day (compressive strength) | Min 52.5-Max | 52.9MPa |
| Soundness | Max 10mm | 0.8mm |
Phase Composition
| Tri Calcium Silicate | C3S> 52 | 60.6% |
| Di Calsium Silicate | C2S | 10% |
| Tri Calcium Aluminate | C3A | 9.5% |
| Tetra Calcium Aluminum Ferrite | C4AF | 10.8% |